OK ARISTOROD 12.50/ER70S-6
Typical Tensile Properties
Elongation | 26 % |
Tensile Strength | 560 MPa |
Testing Condition | As Welded |
Yield Strength | 470 MPa |
分類
CLASSIFICATIONS Weld Metal | |
EN ISO 14341-A | G 38 2 C1 3Si1 |
EN ISO 14341-A | G 42 4 M21 3Si1 |
JIS Z 3312 | G49A0C12 (valid for items ending with H) |
CLASSIFICATIONS Wire Electrode | |
EN ISO 14341-A | G3Si1 |
SFA/AWS A5.18 | ER70S-6 |
CAN/CSA-ISO 14341 | B-G 49A 3 C G6 |
JIS Z 3312 | YGW 12 (C1) |
夏比V型缺口沖擊性能
Impact Value | 130 J |
Testing Condition | As Welded |
Testing Temp | +20 °C |
Impact Value | 90 J |
Testing Condition | As Welded |
Testing Temp | -20 °C |
Impact Value | 70 J |
Testing Condition | As Welded |
Testing Temp | -30 °C |
熔敷數(shù)據(jù)
安培 | 120-380 A |
熔敷率 | 1.3-8.0 kg/h |
電壓 V | 18-35 V |
直徑 | 1.2 mm |
送絲速度 | 2.5-15 m/min |
安培 | 150-420 A |
熔敷率 | 1.6-8.7 kg/h |
電壓 V | 22-36 V |
直徑 | 1.4 mm |
送絲速度 | 2.3-12 m/min |
安培 | 225-550 A |
熔敷率 | 2.1-11.4 kg/h |
電壓 V | 28-38 V |
直徑 | 1.6 mm |
送絲速度 | 2.3-15 m/min |
安培 | 60-200 A |
熔敷率 | 0.8-2.5 kg/h |
電壓 V | 18-24 V |
直徑 | 0.8 mm |
送絲速度 | 3.2-10 m/min |
安培 | 70-250 A |
熔敷率 | 0.8-3.3 kg/h |
電壓 V | 18-26 V |
直徑 | 0.9 mm |
送絲速度 | 3.0-12 m/min |
安培 | 80-300 A |
熔敷率 | 1.0-5.5 kg/h |
電壓 V | 18-32 V |
直徑 | 1 mm |
送絲速度 | 2.7-15 m/min |