產(chǎn)品詳情
CARBO 6W各種刃口堆焊使用
特 性
高鉻成份,耐磨耗耐龜裂性能優(yōu)良,焊后硬度較高,機械加工困難. High chrome component, abrasion resistance, resistance to crack excellent perbance after welding, machining difficulty high hardness.
用 途
淬火硬化模具鋼刃口的修補,適用于SKD11合金工具鋼,淬火后的模具鋼修補. Quench hardened steel blade of repair, applicable to SKD11 alloy steel, alloy after quenching repair.
規(guī) 格
2.6￠ 3.2￠ 4.0￠
TM-2000模具硬化堆焊用
特 性
對沖壓模的金屬磨耗非常有效,焊金第一次為奧氏體組織,第二層為高硬度的馬氏體組織.火焰淬火鋼也可以直接堆焊. The bl stamping mould for abrasion is very effective for the first time, welding gold austenitic organization, the second is the high hardness martensite steel quenching. Flame may also directly hardfacing.
用 途
直接堆焊各種鑄鐵材的模具. All sorts of cast iron material directly surfacing of mould.
規(guī) 格
2.6￠ 3.2￠ 4.0￠ 5.0￠
GNK-8C打底焊條
特 性
高鉻成份,焊金具有高拉力,高韌性 HB-280. High chrome component, high strength, welding gold high toughness HB - 280.
用 途
鑄鋼模硬面制做打底緩沖層,裂縫敏感度較高的特種鋼接合襯焊使用. Cast steel hardfaced making render buffer layer, crack sensitive use of special steel lining welding joints.
規(guī) 格
2.6￠ 3.2￠
CARBO 6W各種刃口堆焊使用
|
特 性 |
高鉻成份,耐磨耗耐龜裂性能優(yōu)良,焊后硬度較高,機械加工困難. High chrome component, abrasion resistance, resistance to crack excellent perbance after welding, machining difficulty high hardness. |
|
用 途 |
淬火硬化模具鋼刃口的修補,適用于SKD11合金工具鋼,淬火后的模具鋼修補. Quench hardened steel blade of repair, applicable to SKD11 alloy steel, alloy after quenching repair. |
|
規(guī) 格 |
2.6￠ 3.2￠ 4.0￠ |
特 性
對沖壓模的金屬磨耗非常有效,焊金第一次為奧氏體組織,第二層為高硬度的馬氏體組織.火焰淬火鋼也可以直接堆焊. The bl stamping mould for abrasion is very effective for the first time, welding gold austenitic organization, the second is the high hardness martensite steel quenching. Flame may also directly hardfacing.
用 途
直接堆焊各種鑄鐵材的模具. All sorts of cast iron material directly surfacing of mould.
規(guī) 格
2.6￠ 3.2￠ 4.0￠ 5.0￠
特 性
高鉻成份,焊金具有高拉力,高韌性 HB-280. High chrome component, high strength, welding gold high toughness HB - 280.
用 途
鑄鋼模硬面制做打底緩沖層,裂縫敏感度較高的特種鋼接合襯焊使用. Cast steel hardfaced making render buffer layer, crack sensitive use of special steel lining welding joints.
規(guī) 格
2.6￠ 3.2￠